Pengaruh Kecepatan Kawat Pengumpan Pada Pengelasan GMAW untuk Pengelasan Pipa Air Boiler Baja Karbon Rendah Terhadap Kekuatan Tarik Sambungan Pengelasan di PT.Z
Kata Kunci:
Kecepatan kawat, pengelasan, baja karbonAbstrak
This research aims to determine the effect of feed wire speed on the tensile strength of low carbon steel welding results using the GMAW method and also to determine the shape of the welding seam on the tensile strength of the welding joint. In this study, the most suitable test results were obtained from the three test results that had been carried out, namely by using a wire speed of 90 cm/minute with a tensile test result of 0.66 Kgf/mm2. The best seam results are by using a U seam with a tensile strength of 0.71 Kgf/mm2. The benefits of the research can be to find out the appropriate wire speed in the process of welding low carbon steel using the GMAW method and to know the tensile strength of the welded seam shape.
Referensi
[1] E. Nugroho, U. Surya Dharma, And S. Karuniawan, “Analisis Pengaruh Ketebalan Plat Baja Karbon Rendah Dan Lama Penekanan Pada Pengelasan Titik (Spot Welding) Terhadap Nilai Kekuatan Tarik,” Vol. 7, No. 1, 2018.
[2] R. M. Ratlalan, Z. Sudirman, And H. Darmadi, “Pengaruh Kekuatan Impak Material Baja St37 Terhadap Kuat Arus Pengelasan Smaw 80 Dan 85 Ampere,” Jurnal Mekanova : Mekanikal, Inovasi Dan Teknologi, Vol. 9, No. 1, Pp. 1–5, 2023.
[3] H. Darmadi, N. Nelza, M. Iqbal, H. Muslim Siregar, D. Kurnia, And Y. Bastanta, “Jurnal Ilmiah Teknik Mesin, Elektro Dan Komputer Analisa Laju Korosi Ketebalan Pipa Baja Karbon Pada Proses Pembakaran Di Unit Boiler,” Juritek, Vol. 3, No. 1, Pp. 64–70, 2023.
[4] M. Z. Yahya, “Pengaruh Variasi Arus Dan Kecepatan Aliran Gas Pelindung Pada Pengelasan Material Ss-304 Menggunakan Las Tig Terhadap Kekuatan Tarik Dan Struktur Mikro,” Jtm, Vol. 9, No. 1, Pp. 145–150, 2021.
[5] E. Tambing, T. Pagasis, O. T. Ranteallo, D. Mangallo, S. P. Siregar, And A. Agustinus, “Analisis Pengaruh Arus Listrik Dan Elektroda Terhadap Kekuatan Dan Kekerasan Pada Proses Pengelasan Smaw Baja Karbon Rendah,” G-Tech: Jurnal Teknologi Terapan, Vol. 8, No. 2, Pp. 878–886, Apr. 2024, Doi: 10.33379/Gtech.V8i2.4070.
Unduhan
Diterbitkan
Terbitan
Bagian
Lisensi
Hak Cipta (c) 2025 Manahan Hutagalung, Daniel Sirait
Artikel ini berlisensiCreative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.